1. Fysisk adsorption och ytladdningsreglering
Vattenreducerande medelmolecules adsorbed on the surface of cement particles, make the particles negatively charged, through electrostatic repulsion to destroy the flocculation structure of cement paste. The cement particles are dispersed from each other due to the repulsion of the homogeneous charge, releasing the free water that is encapsulated, thus enhancing the fluidity. In this process, a significant increase in zeta potential är en nyckelindikator på ökad repulsion .
2. Rums motståndseffekt
Polykarboxylat superplastisatorerform a three-dimensional barrier by adsorbing to cement particles through the main chain and stretching the side chains. Its long chain structure spreads in water and prevents particles from regrouping through spatial site resistance. This effect is especially prominent in low water-cement ratio conditions, can achieve higher dispersion efficiency, and less affected by temperature.
3. vattenfilmsmörjning
Det fria vattnet som frigörs av vattenreducerande medel bildar en smörjande vattenfilm på partiklarnas yta, vilket ytterligare minskar friktionsmotståndet och förbättrar fluiditeten och pumpens prestanda . samtidigt reducerar den enhetliga fördelningen av vatten lokala defekter och optimerar mikrostrukturen .}}
4. Indirekt reglering av hydreringsreaktion
Vattenreducerande medelGenom spridningseffekten för att försena den tidiga hydreringen av cement, minska koncentrationen av hydreringsvärme, men senare på grund av den förtätningsförbättringen men påskyndar utvecklingen av styrka .